R05200 R05400 Dị Ọcha Dị Elu TA1 0.5mm Ọkpụrụkpụ Tantalum Plate TA Ọnụahịa mpempe akwụkwọ TA
Usoro Ngwaahịa
| ihe | Mpempe akwụkwọ tantalum e ji ígwè rụọ nke R05200 R05400 dị ọcha nke 99.95% dị maka ọrịre |
| Ịdị ọcha | Nkeji 99.95% |
| Ọkwa | R05200, R05400, R05252, R05255, R05240 |
| Ọkọlọtọ | ASTM B708, GB/T 3629 |
| Usoro | 1. A na-akpọgharị ọkụ/A na-akpọgharị oyi; 2. Nhicha Alkali; 3. A na-eji elektrọnik eme ihe; 4. Ịrụ ọrụ, ịkpụcha; 5. Ịkwụsị nrụgide |
| Elu | A na-egweri ya nke ọma, na-akpụ ya |
| Ngwaahịa ahaziri ahazi | Dịka eserese si kwuo, ihe ndị a chọrọ maka onye na-eweta ngwaahịa na onye zụrụ ya. |
| atụmatụ | nnukwu ductility, iguzogide nchara, oke ike |
| Ngwa | Mmanụ, Ụgbọelu, Mekaniki, Kemịkal |
Nkọwapụta
| Akụkụ | |||
| ihe | Ọkpụrụkpụ/mm | Obosara/mm | Ogologo/mm |
| Foil | 0.05 | 300 | >200 |
| Mpempe akwụkwọ | 0.1--0.5 | 30- 609.6 | 30-1000 |
| Efere | 0.5--10 | 50-1000 | Afọ 50-2000 |
Ihe achọrọ maka igwe
| Ọkwa na nha | A gbajiri agbaji | ||
| Ike ọdụdọnkeji, psi (MPa) | Ike mmepụta kacha nta, psi (MPa)(2%) | Ogologo nkeji, % (Ogologo nha 1 inch) | |
| Mpempe akwụkwọ, foil. na osisi (RO5200, RO5400) Ọkpụrụkpụ <0.060"(1.524mm)Ọkpụrụkpụ ≥0.060"(1.524mm) | 30000 (207) | 20000 (138) | 20 |
| 25000 (172) | 15000 (103) | 30 | |
| Ta-10W (RO5255)Mpempe akwụkwọ, foil na osisi | 70000 (482) | 60000 (414) | 15 |
| 70000 (482) | 55000 (379) | 20 | |
| Ta-2.5W (RO5252)Ọkpụrụkpụ <0.125" (3.175mm) Ọkpụrụkpụ ≥0.125" (3.175mm) | 40000 (276) | 30000 (207) | 20 |
| 40000 (276) | 22000 (152) | 25 | |
| Ta-40Nb (RO5240)Ọkpụrụkpụ <0.060"(1.524mm) | 40000 (276) | 20000 (138) | 25 |
| Ọkpụrụkpụ>0.060"(1.524mm) | 35000 (241) | 15000 (103) | 25 |
Ngwakọta kemịkalụ
| Kemịstrị (%) | |||||||||||||
| Nhọpụta | Isi ihe mejupụtara ya | Ihe ndị na-adịghị ọcha kachasị | |||||||||||
| Ta | Nb | Fe | Si | Ni | W | Mo | Ti | Nb | O | C | H | N | |
| Ta1 | Ihe fọdụrụ | 0.004 | 0.003 | 0.002 | 0.004 | 0.006 | 0.002 | 0.03 | 0.015 | 0.004 | 0.0015 | 0.002 | |
| Ta2 | Ihe fọdụrụ | 0.01 | 0.01 | 0.005 | 0.02 | 0.02 | 0.005 | 0.08 | 0.02 | 0.01 | 0.0015 | 0.01 | |
atụmatụ
* Ezigbo ductility
* Ezigbo plastik
* Ezigbo iguzogide acid
* Ebe agbaze dị elu, ebe esi mmiri dị elu
* Obere ọnụọgụ nke mgbasawanye okpomọkụ dị obere
* Ezigbo ikike ịmịkọrọ na ịtọhapụ hydrogen
Ngwa
A na-eji Tantalum emepụta ụdị alloys dị iche iche nwere oke agbaze agbaze, ike na ịdị nro.
Site n'ịgwakọta ya na ígwè ndị ọzọ, anyị nwere ike imepụta ngwaọrụ carbide e ji simenti rụọ maka nhazi ígwè, akụkụ injin jet, akụrụngwa nhazi kemịkalụ, ihe nrụpụta nuklia, akụkụ ngwa agha, ihe mgbanwe okpomọkụ, superalloys maka tankị na akpa, wdg. Ejiri ya mee ihe maka ebumnuche.
Ngwaahịa ndị metụtara ya
-
NiNb Nickle Niobium master alloy NiNb60 NiNb65 ...
Nha Ngwaahịa Nickel Niobium Master Alloy Spec (nha: 5-100mm) Nb SP Ni Fe Ta Si C Al 55-66% 0.01% kacha 0.02% Nhazi kachasị 1.0% kacha 0.25% kacha 0.25% kacha 0.05% kacha 1.5% kacha Ti NO Pb As BI Sn 0.05% kacha 0.05% kacha 0.1% kacha 0.005% kacha 0.005% kacha 0.005% kacha 0.005% kacha 0.005% kacha 1.005% kacha 1. Ihe kacha...
-
Ọnụ ahịa ígwè Chromium Chromium CR
Ihe mejupụtara kemịkalụ nke ígwè Chromium Lump/Cr Lmup % Cr Fe Si Al Cu CSP Pb Sn Sb Bi Dịka NHO ≧ ≦ JCr99.2 99.2 0.25 0.25 0.10 0.003 0.01 0.01 0.005 0.0005 0.0005 0.0008 0.0005 0.001 0.01 0.005 0.2 JCr99-A 99.0 0.30 0.25 0.30 0.005 0.01 0.01 0.005 0.0005 0.001 0.001 0.0005 0.001 0.02 0.005 0.3 JCr99-B 99.0 0.40 ...
-
Ogwe akụkụ anọ Tungsten 99.8%
Paramita Ngwaahịa Aha Ngwaahịa Tungsten akụkụ anọ Ogwe ihe Tungsten Ejirila aka ya mee ka ọ dị larịị Njupụta 19.3g/cm3 Njirimara Njupụta dị elu, ezigbo igwe eji arụ ọrụ, ezigbo ihe eji arụ ọrụ, ikike ịmịkọrọ ihe dị elu megide ụzarị X na ụzarị gamma Ịdị ọcha W≥99.95% Nha Dịka arịrịọ gị si dị Nkọwa Ngwaahịa Onye nrụpụta na-enye ya Elu mma 99.95% Tungsten rect...
-
Ụlọ ọrụ mmepụta ihe 0.05mm~2.00mm 99.95% Kwa Kg Emebere ya nke ọma ...
Nkọwapụta Rand WAL1,WAL2 W1,W2 Waya ojii Waya ọcha Min Dayameta (mm) 0.02 0.005 0.4 Oke Dayameta (mm) 1.8 0.35 0.8 Nkọwa Ngwaahịa 1. Ịdị ọcha:99.95% W1 2. Njupụta: 19.3g/cm3 3. Ọkwa: W1,W2,WAL1,WAL2 4. Ọdịdị: dị ka eserese gị. 5. Njirimara: Ebe agbaze dị elu, iguzogide oxidation okpomọkụ dị elu, ndụ ọrụ ogologo, iguzogide ire ere ...
-
Ọnụ ahịa HSG Ferro Tungsten maka ọrịre ferro wolfram...
Anyị na-enye Ferro Tungsten nke ọkwa niile dịka ndị a Grade FeW 8OW-A FeW80-B FEE 80-CW 75%-80% 75%-80% 75%-80% C 0.1% kacha 0.3% kacha 0.6% kacha P 0.03% kacha 0.04% kacha 0.05% kacha S 0.06% kacha 0.07% kacha 0.08% kacha Si 0.5% kacha 0.7% kacha 0.7% kacha Mn 0.25% kacha 0.35% kacha 0.5% kacha Sn 0.06% kacha 0.08% kacha 0.1% kacha Cu 0.1% kacha 0.12% kacha 0.15% kacha Dị ka 0.06% kacha 0.08% m...
-
Astm B392 r04200 Ụdị1 Nb1 99.95% Niobium Rod P...
Paramita Ngwaahịa Aha ngwaahịa ASTM B392 B393 Elu Ọcha Niobium Rod Niobium Bar nwere Ọnụ Ahịa Kachasị Mma Ọcha Nb ≥99.95% Ọkwa R04200, R04210, R04251, R04261, Nb1, Nb2 Standard ASTM B392 Nha ahaziri Ebe agbaze 2468 ogo centigrade Ebe esi mmiri 4742 ogo centigrade Uru ♦ Obere njupụta na Ike Pụrụ Iche Dị Elu♦ Ezigbo Nguzogide Nrụgide ♦ Ezigbo iguzogide mmetụta nke okpomọkụ ♦ Enweghị magnetik na Enweghị nsí...